Corrosion Resistant Hot Rolled Inconel 625 Plate High Strength Nickel Base 625 Sheet

MOQ:	50
Price:	12.35

Details Information

Product Description

Detail Information

Certification

AISI, ASTM

Model Number:

Inconel 625

Shape:

Flat

Technique:

Hot Rolled

Surface Treatment:

Polished

Specification:

1220*2440, 1500*3000, 1500*6000, 2000*6000mm

Nickel Content:

58.0 Min.

Chromium Content:

20.0 Min.-23.0 Max.

Molybdenum Content:

8.0 Min.-10.0 Max.

Niobium Content:

3.15 Min.-4.15 Max.

Density:

8.44 G/cm3

Melting Range:

2350 - 2460°F (1290 - 1350°C)

Yield Strength:

65,000 Psi (min.)

Ultimate Tensile Strength:

125,000 Psi (min.)

Elongation:

50% (min.)

Hardness:

200 Brinell (max.)

Highlight:

Corrosion Resistant Inconel 625 Plate

Hot Rolled Alloy 625 Sheet

High Strength Nickel Base 625 Plate

Product Description

Inconel 625 Alloy 625 DIN2.4856 Plate & Sheet

Manufactured in USA by SMC/ATI/HAYNES

General Properties

Alloy 625 is an austenitic nickel-chromium-molybdenum-niobium alloy offering exceptional corrosion resistance combined with high strength from cryogenic temperatures to 1800°F (982°C). The alloy's strength comes from solid-solution hardening by molybdenum and niobium, eliminating the need for precipitation-hardening treatments.

This chemical composition provides outstanding corrosion resistance in severe operating environments, with excellent resistance to oxidation, carburization, pitting, crevice corrosion, impingement corrosion, intergranular attack, and near-immunity to chloride stress corrosion cracking.

Applications

Aerospace Components: bellows, expansion joints, ducting systems, jet engine exhaust systems, engine thrust-reversers, turbine shroud rings
Air Pollution Control: chimney liners, dampers, flue gas desulfurization (FGD) components
Chemical Processing: equipment handling both oxidizing and reducing acids, super-phosphoric acid production
Marine Service: steam line bellows, Navy ship exhaust systems, submarine auxiliary propulsion systems
Nuclear Industry: reactor core and control rod components, waste reprocessing equipment
Offshore Oil and Gas Production: waste flare gas stacks, piping systems, riser sheathing, sour gas piping and tubing
Petroleum Refining: waste flare gas stacks
Waste Treatment: waste incineration components

Standards

ASTM: B 443 | ASME: SB 443 | AMS: 5599

Chemical Composition

Weight % (all values are maximum unless a range is indicated)

Element	Content	Element	Content
Nickel	58.0 min.	Silicon	0.50
Chromium	20.0 min.-23.0 max.	Phosphorus	0.015
Molybdenum	8.0 min.-10.0 max.	Sulfur	0.015
Iron	5.0	Aluminum	0.40
Niobium (plus Tantalum)	3.15 min.-4.15 max.	Titanium	0.40
Carbon	0.10	Cobalt (if determined)	1.0
Manganese	0.50

Physical Properties

Property	Imperial Units	Metric Units
Density	0.305 lbs/in³	8.44 g/cm³
Specific Heat	0.102 BTU/lb-°F (32-212°F)	427 J/kg-°K (0-100°C)
Modulus of Elasticity	30.1 x 10⁶ psi	207.5 GPa
Thermal Conductivity	75 BTU/hr/ft²/ft/°F	10.8 W/m-°K
Melting Range	2350 - 2460°F	1290 - 1350°C
Electrical Resistivity	50.8 Microhm-in at 70°C	128.9 Microhm-cm at 210°C

Thermal Expansion

Temperature	Mean Coefficient
200°F (93°C)	7.1 x 10⁻⁶ in/in/°F \| 12.8 x 10⁻⁶ cm/cm°C
400°F (204°C)	7.3 x 10⁻⁶ in/in/°F \| 13.1 x 10⁻⁶ cm/cm°C
600°F (316°C)	7.4 x 10⁻⁶ in/in/°F \| 13.3 x 10⁻⁶ cm/cm°C
800°F (427°C)	7.6 x 10⁻⁶ in/in/°F \| 13.7 x 10⁻⁶ cm/cm°C
1000°F (538°C)	7.8 x 10⁻⁶ in/in/°F \| 14.0 x 10⁻⁶ cm/cm°C
1200°F (649°C)	8.2 x 10⁻⁶ in/in/°F \| 14.8 x 10⁻⁶ cm/cm°C
1400°F (760°C)	8.5 x 10⁻⁶ in/in/°F \| 15.3 x 10⁻⁶ cm/cm°C
1600°F (871°C)	8.8 x 10⁻⁶ in/in/°F \| 15.8 x 10⁻⁶ cm/cm°C
1700°F (927°C)	9.0 x 10⁻⁶ in/in/°F \| 16.2 x 10⁻⁶ cm/cm°C

Mechanical Properties

Typical Values at 68°F (20°C)

Yield Strength (0.2% Offset)	Ultimate Tensile Strength	Elongation in 2 in.	Hardness
65,000 psi (448 MPa)	125,000 psi (862 MPa)	50%	200 Brinell (max)

Corrosion Resistance

Alloy 625's highly alloyed composition provides exceptional corrosion resistance in severe environments. The alloy is virtually immune to attack in mild conditions including atmosphere, fresh and sea water, neutral salts, and alkaline solutions. Nickel and chromium provide resistance to oxidizing solutions, while nickel and molybdenum supply resistance in non-oxidizing environments.

Pitting Resistance Equivalency Numbers (PREN)

Alloy	Ni	Cr	Mo	W	Nb	N	PREN
316 Stainless Steel	12	17	2.2	-	-	-	20.4
317 Stainless Steel	13	18	3.8	-	-	-	23.7
Alloy 825	42	21.5	3	-	-	-	26.0
Alloy 625	62	22	9	-	3.5	-	40.8
Alloy C-276	58	16	16	3.5	-	-	45.2

Fabrication Data

Hot Forming

Hot-working temperature range: 1650 - 2150°F (900 - 1177°C). Heavy working should occur near 2150°F (1177°C), with lighter working down to 1700°F (927°C). Use uniform reductions to prevent duplex grain structure.

Cold Forming

Alloy 625 can be cold-formed using standard shop practices in the annealed condition. Work hardening rates are higher than austenitic stainless steels.

Welding

Readily welded by GTAW (TIG), PLASMA, GMAW (MIG/MAG), SAW and SMAW (MMA). No post weld heat treatment required. Brushing with stainless steel wire brush removes heat tint.

Machining

Machine in annealed condition using low cutting speeds with continuous tool engagement. Adequate cut depth prevents contact with work-hardened zones.

Packaging

Tags:

0.12mm 304 Stainless Steel Sheet,

316L 304 ss sheet metal,

0.1mm SS304 Stainless Steel Sheet

317L Stainless Steel Plate Hot Rolled 3-10mm Chemical Composition of 317l Stainless Steel

Contact Now

SUS440A S44002 Martensitic Stainless Steel Plate 3.0mm 4.0mm Hot Rolled 9Cr18Mo Plate

Contact Now

Corrosion Resistant Alloy 317L (UNS S31703) W. Nr. 1.4438 Stainless Steel Plate 415006000mm

Contact Now

Stainless Steel 317L Plate ASTM ASME AISI317L DIN1.4438 8MM Thickness 1000-2000mm

Contact Now

Hot Rolled SUS440A 440B 440C Stainless Steel Plate 9Cr18Mo Steel Plate Cutting

Contact Now

Hot Rolled 400 Series 416 UNS S41600 Martensitic Free Machining Stainless Steel Plate 6-80mm

Contact Now

Hot Rolled ASTM A240 A240M SS Plate 12Cr13 SUS410 AISI 410 6m 10mm 8mm 1500*6000mm

Contact Now

PRODUCTS DETAILS

Products

Cold Rolled Stainless Steel Sheet

Hot Rolled Stainless Steel Plate

Stainless Steel Checkered Plate

Stainless Steel Strip Coil

Stainless Steel Welded Tube

Stainless Steel Seamless Tube

Stainless Steel Round Bar

Stainless Steel Angle Bar

Stainless Steel Flat Bar

Stainless Steel U Bar

Stainless Steel Square Bar

Stainless Steel Hex Bar

Duplex Stainless Steel

Hastelloy Alloy

Nickel Alloy

Monel Alloy

Nitronic Alloy

Incoloy Alloy

Inconel Alloy

Titanium Alloy

Copper Material

Aluminum Material

Corrosion Resistant Hot Rolled Inconel 625 Plate High Strength Nickel Base 625 Sheet

MOQ:	50
Price:	12.35

Detail Information

Product Description

Detail Information

Certification

AISI, ASTM

Model Number:

Inconel 625

Shape:

Flat

Technique:

Hot Rolled

Surface Treatment:

Polished

Specification:

1220*2440, 1500*3000, 1500*6000, 2000*6000mm

Nickel Content:

58.0 Min.

Chromium Content:

20.0 Min.-23.0 Max.

Molybdenum Content:

8.0 Min.-10.0 Max.

Niobium Content:

3.15 Min.-4.15 Max.

Density:

8.44 G/cm3

Melting Range:

2350 - 2460°F (1290 - 1350°C)

Yield Strength:

65,000 Psi (min.)

Ultimate Tensile Strength:

125,000 Psi (min.)

Elongation:

50% (min.)

Hardness:

200 Brinell (max.)

Minimum Order Quantity:

Price:

12.35

Highlight

Corrosion Resistant Inconel 625 Plate

Hot Rolled Alloy 625 Sheet

High Strength Nickel Base 625 Plate

Product Description

Inconel 625 Alloy 625 DIN2.4856 Plate & Sheet

Manufactured in USA by SMC/ATI/HAYNES

General Properties

Applications

Aerospace Components: bellows, expansion joints, ducting systems, jet engine exhaust systems, engine thrust-reversers, turbine shroud rings
Air Pollution Control: chimney liners, dampers, flue gas desulfurization (FGD) components
Chemical Processing: equipment handling both oxidizing and reducing acids, super-phosphoric acid production
Marine Service: steam line bellows, Navy ship exhaust systems, submarine auxiliary propulsion systems
Nuclear Industry: reactor core and control rod components, waste reprocessing equipment
Offshore Oil and Gas Production: waste flare gas stacks, piping systems, riser sheathing, sour gas piping and tubing
Petroleum Refining: waste flare gas stacks
Waste Treatment: waste incineration components

Standards

ASTM: B 443 | ASME: SB 443 | AMS: 5599

Chemical Composition

Weight % (all values are maximum unless a range is indicated)

Element	Content	Element	Content
Nickel	58.0 min.	Silicon	0.50
Chromium	20.0 min.-23.0 max.	Phosphorus	0.015
Molybdenum	8.0 min.-10.0 max.	Sulfur	0.015
Iron	5.0	Aluminum	0.40
Niobium (plus Tantalum)	3.15 min.-4.15 max.	Titanium	0.40
Carbon	0.10	Cobalt (if determined)	1.0
Manganese	0.50

Physical Properties

Property	Imperial Units	Metric Units
Density	0.305 lbs/in³	8.44 g/cm³
Specific Heat	0.102 BTU/lb-°F (32-212°F)	427 J/kg-°K (0-100°C)
Modulus of Elasticity	30.1 x 10⁶ psi	207.5 GPa
Thermal Conductivity	75 BTU/hr/ft²/ft/°F	10.8 W/m-°K
Melting Range	2350 - 2460°F	1290 - 1350°C
Electrical Resistivity	50.8 Microhm-in at 70°C	128.9 Microhm-cm at 210°C

Thermal Expansion

Temperature	Mean Coefficient
200°F (93°C)	7.1 x 10⁻⁶ in/in/°F \| 12.8 x 10⁻⁶ cm/cm°C
400°F (204°C)	7.3 x 10⁻⁶ in/in/°F \| 13.1 x 10⁻⁶ cm/cm°C
600°F (316°C)	7.4 x 10⁻⁶ in/in/°F \| 13.3 x 10⁻⁶ cm/cm°C
800°F (427°C)	7.6 x 10⁻⁶ in/in/°F \| 13.7 x 10⁻⁶ cm/cm°C
1000°F (538°C)	7.8 x 10⁻⁶ in/in/°F \| 14.0 x 10⁻⁶ cm/cm°C
1200°F (649°C)	8.2 x 10⁻⁶ in/in/°F \| 14.8 x 10⁻⁶ cm/cm°C
1400°F (760°C)	8.5 x 10⁻⁶ in/in/°F \| 15.3 x 10⁻⁶ cm/cm°C
1600°F (871°C)	8.8 x 10⁻⁶ in/in/°F \| 15.8 x 10⁻⁶ cm/cm°C
1700°F (927°C)	9.0 x 10⁻⁶ in/in/°F \| 16.2 x 10⁻⁶ cm/cm°C

Mechanical Properties

Typical Values at 68°F (20°C)

Yield Strength (0.2% Offset)	Ultimate Tensile Strength	Elongation in 2 in.	Hardness
65,000 psi (448 MPa)	125,000 psi (862 MPa)	50%	200 Brinell (max)

Corrosion Resistance

Pitting Resistance Equivalency Numbers (PREN)

Alloy	Ni	Cr	Mo	W	Nb	N	PREN
316 Stainless Steel	12	17	2.2	-	-	-	20.4
317 Stainless Steel	13	18	3.8	-	-	-	23.7
Alloy 825	42	21.5	3	-	-	-	26.0
Alloy 625	62	22	9	-	3.5	-	40.8
Alloy C-276	58	16	16	3.5	-	-	45.2

Fabrication Data

Hot Forming

Cold Forming

Alloy 625 can be cold-formed using standard shop practices in the annealed condition. Work hardening rates are higher than austenitic stainless steels.

Welding

Readily welded by GTAW (TIG), PLASMA, GMAW (MIG/MAG), SAW and SMAW (MMA). No post weld heat treatment required. Brushing with stainless steel wire brush removes heat tint.

Machining

Machine in annealed condition using low cutting speeds with continuous tool engagement. Adequate cut depth prevents contact with work-hardened zones.