| Surface Finish | Characteristics and Application |
|---|---|
| NO.2B | Better brightness and flatness than NO.2D, with improved mechanical properties through special surface treatment for comprehensive uses. |
| NO.1 | Surface finished by heat treatment and pickling after hot rolling. |
| NO.4 | Polished with abrasive belt grit #150-#180, featuring better brightness with discontinuous coarse striations. Used for bathtubs, building ornaments, electrical appliances, kitchen utensils, and food processing equipment. |
| HL | Polished with abrasive belt grit #150-#320 on NO.4 finish with continuous streaks. Primarily used for building ornaments, elevators, building doors, and frontal plates. |
| BA | Cold rolled, bright annealed and skin-passed with excellent brightness and mirror-like reflexivity. Ideal for kitchen apparatus and ornaments. |
| 8K | Excellent brightness and superior reflexivity, can be used as a mirror. |
| Property | Value | Property | Value |
|---|---|---|---|
| Tensile Strength σb (MPa) | ≥ 520 | Specific Heat Capacity (0-100°C, KJ/kgK) | 0.50 |
| Yield Strength σ0.2 (MPa) | ≥ 205 | Thermal Conductivity (W/m·K) | 16.3 (100°C), 21.5 (500°C) |
| Elongation δ5 (%) | ≥ 40 | Linear Expansion Coefficient (10⁻⁶/K) | 17.2 (0-100°C), 18.4 (0-500°C) |
| Section Shrinkage ψ (%) | ≥ 60 | Resistivity (20°C, 10⁻⁶ Ω·m) | 0.73 |
| Hardness | ≤ 187HB; ≤ 90HRB; ≤ 200HV | Longitudinal Elastic Modulus (20°C, KN/mm²) | 193 |
| Melting Point (°C) | 1398 - 1454 | Specific Heat Capacity | 0.50 |
|
|
| MOQ: | 50 |
| 価格: | 1.95 |
| Surface Finish | Characteristics and Application |
|---|---|
| NO.2B | Better brightness and flatness than NO.2D, with improved mechanical properties through special surface treatment for comprehensive uses. |
| NO.1 | Surface finished by heat treatment and pickling after hot rolling. |
| NO.4 | Polished with abrasive belt grit #150-#180, featuring better brightness with discontinuous coarse striations. Used for bathtubs, building ornaments, electrical appliances, kitchen utensils, and food processing equipment. |
| HL | Polished with abrasive belt grit #150-#320 on NO.4 finish with continuous streaks. Primarily used for building ornaments, elevators, building doors, and frontal plates. |
| BA | Cold rolled, bright annealed and skin-passed with excellent brightness and mirror-like reflexivity. Ideal for kitchen apparatus and ornaments. |
| 8K | Excellent brightness and superior reflexivity, can be used as a mirror. |
| Property | Value | Property | Value |
|---|---|---|---|
| Tensile Strength σb (MPa) | ≥ 520 | Specific Heat Capacity (0-100°C, KJ/kgK) | 0.50 |
| Yield Strength σ0.2 (MPa) | ≥ 205 | Thermal Conductivity (W/m·K) | 16.3 (100°C), 21.5 (500°C) |
| Elongation δ5 (%) | ≥ 40 | Linear Expansion Coefficient (10⁻⁶/K) | 17.2 (0-100°C), 18.4 (0-500°C) |
| Section Shrinkage ψ (%) | ≥ 60 | Resistivity (20°C, 10⁻⁶ Ω·m) | 0.73 |
| Hardness | ≤ 187HB; ≤ 90HRB; ≤ 200HV | Longitudinal Elastic Modulus (20°C, KN/mm²) | 193 |
| Melting Point (°C) | 1398 - 1454 | Specific Heat Capacity | 0.50 |